Melting Behavior of PA6 and PA6/PE Blends Crystallized from Amorphous State

Aim To investigate the melting behavior of polyamide 6 in polyamide 6/polyethy lene blends crystallized from amorphous state. Methods DSC was used to test effects of annealing temperature, annealing time, DSC scan rate, and the step wise annealing on the melting peaks of the ice water quenched specimens. Results and Conclusion Varied melting peaks of PA6 component were obtained. The degree of perfection and the crystallization degree of PA6 crystals decreased in the blends, and the crystallization degree of PA6 increased with the increasing of the annealing time. The height of the upper melting peak of reference PA6 is higher than that in blends.